Jesmonite AC100 - 1Kg Liquid

Jesmonite AC100 - 1 kg Liquid

Jesmonite AC100 is a water-based composite material used to make decorative molded objects. It is safe to use and contains no solvents or VOCs. It can be cast and laminated using our unique Quadaxial Glass.

Jesmonite AC100 Liquid should be used within twelve months and Jesmonite Base should be used within nine months from the date displayed on the packaging.

Products benefits

• Superior cast and glass-reinforced moldings
• Solvent-free & no VOCs
• Fire resistant
• Lightweight
• Impact resistant

Information

• Easy to use, adaptable material for all molding applications.
• Suitable for decorative cast objects, mold cases, and wall panels.
• Supplied with a range of ancillary products including glass reinforcements, pigments, fillers, and control chemicals to adapt the material to the widest range of applications.
• The ultimate chameleon material can replicate virtually any surface, color, or texture.

Available in:

Kit sizes range from 3.5kg to 35kg. See the product list for the full range of ancillary materials compatible with AC100.

SPECIFICATIONS

• Mix ratio 2.5:1 parts Base to Liquids ratio by weight
• Wet density 1845 kg/m³
• Dry density 1745 kg/m³
• Initial set 15 – 20 minutes (18°C, No Retarder)
• Expansion on set 0.15%

OTHER PROPERTIES

• Compressive strength: 25 – 30 MPa
• Tensile strength (UTS): 25 – 35 Mpa
• Bending elastic limit (LOP): 15 – 20 Mpa
• Bending strength (MOR): 50 – 65 Mpa
• Youngs Modulus: 5 – 6 Mpa
• Impact strength (Charpy): 30 KJ/m²
• Moisture movement: <1%
• EN13501-1 Fire Classification: B-s1-d0
• Freeze/Thaw resistance: Excellent – Test specimens undamaged
• Wet/Dry 50 cycles: Test specimens undamaged

APPLICATION AREAS

Cast and laminated decorative mouldings, and with the inclusion of suitable glass reinforcements AC100 can be used for lightweight, high-impact panels. Jesmonite AC100 provides a fire resistant coating for many expanded foams for theme park and theatre props.

KEY ATTRIBUTES

• Solvent-free – No VOCs
• Good abrasion resistance and impact strength
• High compressive and tensile strength
• Rapid curing and high early strength gain

STORAGE

As a basic rule liquid containers should be kept well sealed to prevent water evaporation and skin forming. They should be stored at a constant temperature between 5 – 25°C and used within twelve months. Freezing must be avoided. The base should be kept dry and stored at 5 – 25°C and used within 9 months.